Columnar defects in YBa₂Cu₃O_7-δ induced by irradiation with high energy heavy ions

Abstract

Defect microstructures in three YBa2Cu3O 7-δ single crystals irradiated with different high energy heavy ions show dramatically different damage morphologies. For Sn and Au projectiles with total energies of 580 MeV and 1.0 GeV, respectively, highly aligned tracks are observed which extend for many microns in the crystals. However, irradiation with 1.4 GeV Br ions results in the formation of spherical damage regions widely separated along the ion path through the entire crystal. The continuity of damage along the ion path for the different projectiles varies with the magnitude of the electronic energy loss.